| 材料 | 抗拉强度 σb(Mpa) | 屈服强度 σs(Mpa) | 硬度 /HB | Density g/cm3 | 伸长率/% |
| 2024-T3/T4 | 470-485 | 325-345 | 120~145 | 2.82 | 10-12 |
| 5052-H32 | 228 | 193 | 60 | 2.68 | 12 |
| 6061-T6 | 310 | 275 | 95 | 2.73 | 6-10 |
| 6063-T5/T6 | 185 | 145 | 95 | 2.73 | 8 |
| 6082-T6 | 245 | 140 | 95 | 2.73 | 10 |
| 7075-T6 | 570 | 505 | 150 | 2.82 | 11 |
| MIC-6 | 166 | 105 | 95 | 2.82 | 11 |
| 材料 | 抗拉强度 σb(Mpa) |
屈服强度 σs(Mpa) |
硬度 /HB | Density g/cm3 |
伸长率/% |
|---|---|---|---|---|---|
| 1010 | 325 | 180 | 137 | 7.85 | 31 |
| 1018 | 453 | 245 | 197 | 7.85 | 14-22.5 |
| 1020 | 500 | 275 | 131 | 7.85 | 25 |
| A3 | 500 | 235 | 150 | 7.85 | 26.5 |
| A8 | 240 | 195 | 45-65 | 7.85 | 32 |
| A36 | 400 | 250 | 160 | 7.85 | 20 |
| 8620 | 1176 | 785 | 197 | 7.9 | 9 |
| 1045 | 625 | 530 | 229 | 7.85 | 16 |
| 4130 | 560-731 | 460 | 229 | 7.85 | 12 |
| 4140 | 1080 | 930 | 217 | 7.85 | 12 |
| 4340 | 745 | 470 | 269 | 7.85 | 12 |
| S7 | 680 | 650 | 215 | 7.85 | 10 |
| SKD-11 | 689 | 655 | 255 | 7.85 | 10 |
| A2 | 689 | 655 | 248 | 7.85 | 10 |
| A10 | 335 | 205 | 137 | 7.85 | 12 |
| D2 | 370 | 210 | 255 | 7.85 | 13 |
| 8620 | 1176 | 785 | 261 | 7.85 | 9 |
| 材料 | 抗拉强度 σb(Mpa) |
屈服强度 σs(Mpa) |
硬度 /HB | Density g/cm3 |
伸长率/% |
|---|---|---|---|---|---|
| 201 | 750 | 230 | 183 | 7.64-7.93 | 55-60 |
| SS304 | 517 | 206 | 201 | 7.93 | 40 |
| 303 | 515 | 205 | 90-100 | 7.93 | 40 |
| 316 | 580 | 172 | 187 | 7.98 | 40 |
| 316L | 485 | 170 | 180 | 7.98 | 40 |
| 15-5PHSS | 550 | 200 | 187 | 7.93 | 40 |
| 17-4PHSS | 930 | 725 | 363 | 7.8 | 16 |
| 17-7PHSS | 1030 | 725 | 380 | 7.93 | 16 |
| 440C | 560 | 250 | 269 | 7.75 | 20 |
| 420 | 635 | 440 | 201 | 7.75 | 20 |
| 材料 | 抗拉强度 σb(Mpa) |
屈服强度 σs(Mpa) |
硬度 /HB | Density g/cm3 |
伸长率/% |
|---|---|---|---|---|---|
| Titanium Ti 6Al-4V | 235 | 140 | 195 | 4.51 | 50-60 |
| Titanium Grade 5 6Al-4V | 1050 | 827 | 195 | 4.5 | 25 |
| Zamark#3 | 283 | 221 | 65-145 | 6.6 | 10 |
| 青铜 | 255 | 69 | 55-70 | 7.5-8.9 | 46-70 |
| 黄铜 | 478 | 239 | 53-56 | 8.5-8.8 | 44-60 |
| 铜合金 | 394 | 258 | 35-45 | 8.89 | 45-50 |
| 更多牌号... | 等... | 等... | 等... | 等... | 等... |
我们的加工服务与一系列广泛的材料兼容，从金属到塑料。根据您的应用，您可以从我们提供的50多种生产级材料中选择。请看我们的数控加工材料清单。您也可以联系我们，咨询特殊定制要求。
铝合金
铝是一种高延展性的金属，使其易于加工。这种材料具有良好的强度-重量比，并有许多类型可供各种应用。
Lead Time: < 10 days
Wall Thickness: 0.50 mm
Tolerances: ±0.01mm (±0.0004″)
Max part size: 200 x 80 x 100 cm
不锈钢
不锈钢是低碳钢，提供了许多工业应用中所追求的特性。不锈钢通常含有至少10%的铬（按重量）。
Lead Time: < 10 days
Wall Thickness: 0.50 mm
Tolerances: ±0.01mm (±0.0004″)
Max part size: 200 x 80 x 100 cm
黄铜
黄铜在许多应用中都具有理想的特性。它摩擦力低，具有优良的导电性，并具有金色（黄铜）的外观。
Lead Time: < 10 days
Wall Thickness: 0.50 mm
Tolerances: ±0.01mm (±0.0004″)
Max part size: 200 x 80 x 100 cm
钛合金
钛具有许多材料特性，使其成为要求苛刻的应用的理想金属。这些特性包括出色的抗腐蚀、抗化学品和抗极端温度。这种金属还具有出色的强度-重量比。
Lead Time: < 10 days
Wall Thickness: 0.50 mm
Tolerances: ±0.01mm (±0.0004″)
Max part size: 200 x 80 x 100 cm
铜合金
铜显示出优良的导热性、导电性和可塑性。它还具有高度的延展性，耐腐蚀，并且容易焊接。
Lead Time: < 10 days
Wall Thickness: 0.50 mm
Tolerances: ±0.01mm (±0.0004″)
Max part size: 200 x 80 x 100 cm
塑料
塑料也是非常受欢迎的数控加工选择，因为其选择范围广，价格相对较低，而且所需的加工时间明显较快。我们提供所有常见塑料的数控加工服务。
| POM | PEEK | HDPE | PET |
| 尼龙 | PTFE | PVC | PP |
| ABS | PC | PMMA |
我们的材料目录包括塑料金属和复合材料制造选项。 我们使用的金属包括铝、镁、钢、钛、铜等。除了我们的库存材料选择外，我们还可以采购所需的材料，并为机加工提供为您定制的原材料。
塑料： ABS, ABS+PC, PC, PP, PEEK, POM, Acrylic (PMMA), Teflon, PS, HDPE, PPS, DHPE, PA6, PA66, PEI, PVC, PET, PPS, PTFE 以及 查看更多可用塑料.
金属材料： 铝、黄铜、铜、镁、钛、不锈钢、锡、锌和其他材料。 点击此处查看更多材料。.
这些是最常见的数控原型和生产零件的材料。此外，我们可以使用你能想象的任何类型的可加工塑料和金属。
上述材料是最常见的生产材料。如果所需的材料没有在上面列出，可联系我们咨询定制材料的报价。
发送图纸，即刻定制生产
7天24小时技术支持
在1小时内将由专业技术人员为您提供快速报价服务
| 材料 | 抗拉强度 σb(Mpa) | 屈服强度 σs(Mpa) | 硬度 /HB | 密度 /cm3 | 伸长率/% | 特点 |
| 2024-T3/T4 | 470-485 | 325-345 | 120~145 | 2.82 | 10-12 | High strength High fatigue resistance |
| 5052-H32 | 228 | 193 | 60 | 2.68 | 12 | High strength High fatigue resistance |
| 6061-T6 | 310 | 275 | 95 | 2.73 | 6-10 | Good weldability Commonly extruded Suitable for hot forging |
| 6063-T5/T6 | 185 | 145 | 95 | 2.73 | 8 | Good weldability Commonly extruded Suitable for hot forging |
| 6082-T6 | 245 | 140 | 95 | 2.73 | 10 | Higher strength Lower ductility Wrought |
| 7075-T6 | 570 | 505 | 150 | 2.82 | 11 | Good fatigue strength Low resistance Good corrosion resistance High strength-to-density ratio |
| MIC-6 | 166 | 105 | 95 | 2.82 | 11 | Good corrosion resistant Good formability High intensity |
| 更多牌号... | 等... | 等... | 等... | 等... | 等... | 等... |
| 材料 | 抗拉强度 σb(Mpa) | 屈服强度 σs(Mpa) | 硬度 /HB | 密度 /cm3 | 伸长率/% | 特点 |
|---|---|---|---|---|---|---|
| 1010 | 325 | 180 | 137 | 7.85 | 31 | Good plasticity Good toughness Low strength |
| 1018 | 453 | 245 | 197 | 7.85 | 14-22.5 | Good plasticity Good toughness Low strength |
| 1020 | 500 | 275 | 131 | 7.85 | 25 | Good plasticity Good toughness Low strength |
| A3 | 500 | 235 | 150 | 7.85 | 26.5 | Good combination property |
| A8 | 240 | 195 | 45-65 | 7.85 | 32 | High toughness High plasticity Low strength |
| A36 | 400 | 250 | 160 | 7.85 | 20 | Common welding material Cheap and easy on welding |
| 8620 | 1176 | 785 | 197 | 7.9 | 9 | High hardness High abrasive resistance High fatigue strength |
| 1045 | 625 | 530 | 229 | 7.85 | 16 | Good strength Low hardenability |
| 4130 | 560-731 | 460 | 229 | 7.85 | 12 | High strength Good hardenability Good toughness |
| 4140 | 1080 | 930 | 217 | 7.85 | 12 | High strength High hardenability Good toughness |
| 4340 | 745 | 470 | 269 | 7.85 | 12 | Excellent strength High fatigue strength High toughness |
| S7 | 680 | 650 | 215 | 7.85 | 10 | Good toughness Shock resistance High impact resistance |
| SKD-11 | 689 | 655 | 255 | 7.85 | 10 | High temperature strength High temperature resistance High hardness High wear resistant Good toughness Good hardenability High abrasive resistance |
| A2 | 689 | 655 | 248 | 7.85 | 10 | High abrasion resistance Excellent hardness High toughness |
| A10 | 335 | 205 | 137 | 7.85 | 12 | High abrasion resistance Excellent hardness Excellent toughness |
| D2 | 370 | 210 | 255 | 7.85 | 13 | High impact resistance High abrasive resistance |
| 8620 | 1176 | 785 | 261 | 7.85 | 9 | High temperature strength High temperature resistance High hardness |
| 更多牌号... | 等... | 等... | 等... | 等... | 等... | 等... |
| 材料 | 抗拉强度 σb(Mpa) | 屈服强度 σs(Mpa) | 硬度 /HB | 密度 /cm3 | 伸长率/% | 特点 |
|---|---|---|---|---|---|---|
| 201 | 750 | 230 | 183 | 7.64-7.93 | 55-60 | Good acid/alkali-resisting High density Non-magnetic Pinhole-free |
| SS304 | 517 | 206 | 201 | 7.93 | 40 | Good combination property High corrosion resistance Good heat resistance High acid/alkali-resisting |
| 303 | 515 | 205 | 90-100 | 7.93 | 40 | High corrosion resistance High acid/alkali-resisting |
| 316 | 580 | 172 | 187 | 7.98 | 40 | High corrosion resistance High temperature resistance Excellent acid/alkali-resisting |
| 316L | 485 | 170 | 180 | 7.98 | 40 | High corrosion resistance High temperature resistance Excellent acid/alkali-resisting |
| 15-5PHSS | 550 | 200 | 187 | 7.93 | 40 | Good combination property High corrosion resistance Good heat resistance High acid/alkali-resisting |
| 17-4PHSS | 930 | 725 | 363 | 7.8 | 16 | High strength High corrosion resistance Excellent machinability |
| 17-7PHSS | 1030 | 725 | 380 | 7.93 | 16 | High strength Excellent corrosion resistance Good toughness |
| 440C | 560 | 250 | 269 | 7.75 | 20 | Excellent corrosion resistance High temperature resistance High hardness |
| 420 | 635 | 440 | 201 | 7.75 | 20 | Excellent corrosion resistance High temperature resistance High hardness |
| 更多牌号... | 等... | 等... | 等... | 等... | 等... | 等... |
| 材料 | 抗拉强度 σb(Mpa) | 屈服强度 σs(Mpa) | 硬度 /HB | 密度 /cm3 | 伸长率/% | 特点 |
|---|---|---|---|---|---|---|
| Titanium Ti 6Al-4V | 235 | 140 | 195 | 4.51 | 50-60 | Low density High strength Resistant to corrosion in sea Water, aqua regia, and chlorine. |
| Titanium Grade 5 6Al-4V | 1050 | 827 | 195 | 4.5 | 25 | High tensile strength and toughness Light in weight Extraordinary corrosion resistance The ability to withstand extreme temperatures |
| Zamark#3 | 283 | 221 | 65-145 | 6.6 | 10 | Superior corrosion resistance Low creep strength |
| 青铜 | 255 | 69 | 55-70 | 7.5-8.9 | 46-70 | Ductile High electrical conductivity |
| 黄铜 | 478 | 239 | 53-56 | 8.5-8.8 | 44-60 | High electrical conductivity High malleability Good flow characteristics |
| 铜合金 | 394 | 258 | 35-45 | 8.89 | 45-50 | Thermal High electrical conductivity High ductility |
| 更多牌号... | 等... | 等... | 等... | 等... | 等... | 等... |